If possible you should always perform a power grid on a practice piece to determine the optimum setting.
Cermark laser settings for glass.
There are several laser marking coating types that allow you to offer more options for your customers without having to buy additional marking equipment.
This coating will also create deep black marks at a very wide range of laser power and speed settings.
The most common problem with the cermark process is when the mark washes off.
In order to minimize damage to glass with a co2 laser it is essential to use low power and slower speeds in an attempt to melt the material onto the glass without damaging it.
The type of substrate thickness of the substrate and the substrate s ability to conduct heat will influence the power needed to make a mark on it.
Physical address engravers network 637 107th st arlington tx 76011 engravers network 505 n sam houston pkwy e suite 355 houston tx 77060.
When using cermark metal marking solution remember that not all metals use the same speed setting.
Gcc s400 laser parts.
De 3 rotary engraver parts.
We supply cermark special coatings for use with co2 and fiber laser marking engraving systems to make high contrast permanent marks on metals glass and ceramic items.
Power settings that are too high can melt and distort many materials.
Co2 laser wavelength causes cracking in glass.
This is caused by laser power and speed settings not being correct the laser is out of focus or optics need to be cleaned.
There are numerous variables that affect what settings you should use.
All settings noted use the default resolution which is 500 or 600 depending on the make of your laser system.
Parallel ada specialty.
Much improved glass marking there is a much greater ease of glass marking at a wider range of settings and much less coating thickness will be required.
Every laser is different and you will have to do testing on your system to determine specific power and speed settings for each laser.
It is sometimes difficult to determine the best laser power and speed settings for cermark materials.
Gcc spirit gls hybrid parts.
For example aluminum conducts heat much better than steel so it will.
Gcc mg380 laser parts.
Different types of metal require different power and speed.
Gcc t500 laser parts.